Sissy bar material/surface finish

[Dominik Stawowczyk]

Hello,
I just purchased the sissi bar for my vmax. The person who sell it said that it is chromed, not polished aluminium and magnet catch it a little. I have never seen the steel frame in sissi bar. Is it possible that it is made from steel or somebody chromed the aluminium?
The chrome is not perfect so it is necessary to renovate it. I did not get it yet but I am thinking what to do with the frame. Thanks in advance for feedback if somebody has the chromed sissi.
View attachment 95887

 

[Radioguylogs]

It is aluminum under the chrome.

It would be difficult to remove the chrome. Perhaps you could chrome over chrome?

Maybe other members have some suggestions.

 

[Fire-medic]

If you take it to a chrome shop, they do the reverse-process, which will remove the chrome. Chrome, nickel, copper to return to the aluminum factory finish, Polish/paint to your desire. I have done the reverse-chrome removal on scoops which turned out OK.

 

[Radioguylogs]

If you take it to a chrome shop, they do the reverse-process, which will remove the chrome. Chrome, nickel, copper to return to the aluminum factory finish, Polish/paint to your desire. I have done the reverse-chrome removal on scoops which turned out OK.

Wow, I've never heard of this. Is it expensive?

The 84-86 Honda V65's all have peeling chrome wheels and owners lament how to make them better.

 

[Dominik Stawowczyk]

If you take it to a chrome shop, they do the reverse-process, which will remove the chrome. Chrome, nickel, copper to return to the aluminum factory finish, Polish/paint to your desire. I have done the reverse-chrome removal on scoops which turned out OK.

Thanks for info. I was not aware before that aluminium can be chromed. I would like to keep surface as natural aluminium so if it is feasible to do reverse like you wrote I will do it, later polish aluminium and will paint it with clear lack. I hope the al will looks like the other Yamaha parts.

 

[Fire-medic]

You need to be sure that the shop leaves it in the solution long enough to make the process work. If they don't give it enough time, the material removal will be insufficient and you will not be happy with the uneven results.

Once the de-plating by electrolysis is done, you can polish it with some Simichrome or other metal polish, and wax it to delay the inevitable oxidation, which can only be delayed and removed with periodic re-polishing.

I've posted before about a good paint for aluminum, Alumiblast by Martin Seymour. I use it and I like it. It's formulated for aluminum.



https://www.vmaxforum.net/threads/1988-vmax.52957/#post-531722

Here's a scoop I sanded and painted with Alumiblast.

 

[Dominik Stawowczyk]

You need to be sure that the shop leaves it in the solution long enough to make the process work. If they don't give it enough time, the material removal will be insufficient and you will not be happy with the uneven results.

Once the de-plating by electrolysis is done, you can polish it with some Simichrome or other metal polish, and wax it to delay the inevitable oxidation, which can only be delayed and removed with periodic re-polishing.

I've posted before about a good paint for aluminum, Alumiblast by Martin Seymour. I use it and I like it. It's formulated for aluminum.

View attachment 95892

https://www.vmaxforum.net/threads/1988-vmax.52957/#post-531722

Here's a scoop I sanded and painted with Alumiblast.
View attachment 95893

The sissi bar came. The corrosion of alu rack started to unstick the chrome. I decydent to try with soda Blasting. The guy with those equipment said that the chrome can me remove easily and he did it already so we will see. After chrome will be removed the plan is to polish and then paint with transparent lack to protect in the same way that was done with original. Your alu paint looks really good. Is it abrasion resistant?